Semiconductor device and method of fabricating the same

ABSTRACT

An extension region is formed by ion implantation under masking by a gate electrode, and then a substance having a diffusion suppressive function over an impurity contained in a source-and-drain is implanted under masking by the gate electrode and a first sidewall spacer so as to form amorphous layers a semiconductor substrate within a surficial layer thereof and in alignment with the first sidewall spacer, to thereby form an amorphous diffusion suppressive region.

CROSS-REFERENCE TO RELATED APPLICATIONS

This is a divisional of U.S. application Ser. No. 10/800,749, filed on Mar. 16, 2004, which is based upon and claims the benefit of priority from the prior Japanese Patent Application No. 2003-373499, filed on Oct. 31, 2003, the entire contents of which are incorporated herein by reference.

BACKGROUND OF THE INVENTION

1. Field of the Invention

The present invention relates to a semiconductor device having a gate and source-and-drain, and a method of fabricating the semiconductor device.

2. Description of the Related Art

There is a still further need for micronization of recent semiconductor devices, where efforts have been made typically on a MOS transistor, having an extension structure, in order to make a deep-junction, source-and-drain more shallower.

More specifically, one known technique for forming an n-type MOS transistor is such as implanting arsenic (As) ion, under masking by the gate electrode and sidewall spacer, so as to form amorphous layers the surface of a semiconductor substrate, and then implanting phosphorus (P) ion to the amorphous portion through the same masks, to thereby form an n-type source-and drain (see Patent Document 1). Another known technique for forming a p-type MOS transistor is such as implanting silicon sidewall spacer, so as to form amorphous laysers the surface of a semiconductor substrate, and then implanting boron (B) ion to the amorphous portion through the same masks, to thereby form a p-type source-and drain (see Patent Document 2).

[Patent Document 1]

Japanese Patent Application Laid-Open No. Hei 11-186188

[Patent Document 2]

Japanese Patent Application Laid-Open No. Sho 61-018176

The above-described techniques should surely be successful in making the junction relatively shallower by preliminarily forming amorphous laysers the area where the source-and-drain region is to be formed later. Demands for suppressing lateral diffusion of the impurity contained in the source-and-drain are, however, becoming severer as the micronization of the semiconductor device further advances, and it is also necessary to fulfill requirements for higher performances as well as those for micronization. First, a deep-junction, source-and-drain region must be kept at a certain degree of depth in order to reduce the junction leakage. In addition, the source-and-drain must have a higher impurity concentration in order to reduce the contact resistance and sheet resistance. This inevitably enhances the lateral diffusion, and raises a problem in that the impurity can readily reach the extension region to thereby degrade the roll-off characteristics.

The present invention is conceived after considering the above-described problems, and an object thereof resides in providing a highly-reliable semiconductor device capable of exactly suppressing the lateral diffusion of the source-and-drain, fulfilling the requirements for further micronization and more advanced performances, and a method of fabricating such semiconductor device.

SUMMARY OF THE INVENTION

A semiconductor device of the present invention comprises a gate formed over a semiconductor region while placing an insulating film in between; a first impurity-diffused region formed, as being aligned with the gate, in the surficial layer of the semiconductor region; a second impurity-diffused region formed, as being distant from the gate while placing a portion of a side of the first impurity-diffused region in between; and a third impurity-diffused region formed, as being distant from the gate while placing the portion of the side of the first impurity-diffused region and a portion of a side of the second impurity-diffused region in between; wherein the second impurity-diffused region is formed as containing a diffusion suppressive element for suppressing diffusion of an impurity contained in the third impurity-diffused region.

A method of fabricating a semiconductor device of the present invention comprises the steps of forming a gate over a semiconductor region while placing an insulating film in between: forming a first impurity-diffused region by introducing an impurity into a surficial layer of the semiconductor region under masking by the gate; forming a first sidewall spacer over both lateral faces of the gate; forming an amorphous second impurity-diffused region by introducing a diffusion suppressive element into the surficial layer of the semiconductor region under masking by the gate and the first sidewall spacer; forming a second sidewall spacer to cover the first sidewall spacer over both lateral sides of the gate; and forming a third impurity-diffused region by introducing an impurity into the surficial layer of the semiconductor region to a depth larger than that of the first impurity-diffused region under masking by the gate, the first sidewall spacer and the second sidewall spacer.

BRIEF DESCRIPTION OF THE DRAWINGS

FIGS. 1A and 1B are schematic sectional views for explaining basic configurations of the present invention in comparison with a conventional structure;

FIGS. 2A to 2C are schematic sectional views sequentially showing process steps of a method of fabricating a CMOS transistor of the present embodiment;

FIGS. 3A to 3C are schematic sectional views sequentially showing process steps of the method of fabricating a CMOS transistor of the present embodiment as continued from FIG. 2C;

FIGS. 4A to 4C are schematic sectional views sequentially showing process steps of the method of fabricating a CMOS transistor of the present embodiment as continued from FIG. 3C;

FIGS. 5A and 5B are schematic sectional views sequentially showing process steps of the method of fabricating a CMOS transistor of the present embodiment as continued from FIG. 4C;

FIG. 6 is a graph showing roll-off characteristics expressed by relations between gate length L_(g) and threshold voltage;

FIG. 7 is a graph showing C_(ov) characteristics expressed by relations between depth of diffusion suppressive region and C_(ovn); and

FIG. 8 is a graph showing I_(on)-I_(off) characteristics expressed by relations between ON current (I_(on)) and OFF current (I_(off)).

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS Basic Concept of the Present Invention

First, a basic concept of the present invention will be explained.

For the purpose of exactly suppressing the lateral diffusion of a deep-junction, source-and-drain while ensuring its depth to a proper degree so as to secure a large impurity concentration, the present inventors reached an idea of disposing a diffusion suppressive region (second region) between the extension region (first region) and the source-and-drain (third region) so as to keep their edges distant from each other.

In a conventional MOS transistor, as shown in FIG. 1A, an extension region 3 is formed by ion implantation under masking by a gate electrode 2 formed on a semiconductor region, which is a semiconductor substrate 1 herein, and thereafter a source-and-drain 5 is formed by ion implantation under masking by the gate electrode 2 and a first sidewall spacer 4, where the lateral diffusion of the impurity from the source-and-drain 5 tends to occur as indicated by arrow “A” in the drawing.

In contrast to this, a MOS transistor of the present invention is fabricated, as shown in FIG. 1B, by forming the extension region 3 by ion implantation under masking by the gate electrode 2, and thereafter a substance having a diffusion suppressive function (diffusion suppressive element) over the impurity contained in the source-and-drain 5 is introduced by ion implantation under masking by the gate electrode 2 and the first sidewall spacer 4, so as to form amorphous laysers the semiconductor substrate 1 within a surficial layer thereof and in alignment with the first sidewall spacer 4, to thereby form an amorphous diffusion suppressive region 6. Thereafter, the source-and-drain 5 is formed in a portion of the surficial layer in alignment with a second sidewall spacer 7, under masking by the gate electrode 2, first sidewall spacer 4 and second sidewall spacer 7.

The diffusion suppressive element is at least any one element selected from arsenic (As), germanium (Ge), nitrogen (N), fluorine (F) and carbon (C) for the case where the impurity contained in the extension region 3 and the source-and-drain 5 is an n-type impurity; and is at least any one element selected from germanium (Ge), nitrogen (N), fluorine (F), carbon (C) and indium (In) for the case where the impurity contained in the extension region 3 and the source-and-drain 5 is a p-type impurity.

In this way, the extension region 3 and source-and-drain 5 are kept distant from each other by the diffusion suppressive region 6, and the lateral diffusion of the impurity from the source-and-drain 5 is completely blocked by the diffusion suppressive region 6. It is thus made possible to reduce the junction leakage, contact resistance and sheet resistance even if the source-and-drain is formed so as to have a relatively large depth and impurity concentration to thereby prevent the roll-off characteristic from degrading, and to realize further micronization and higher performances of the MOS transistor.

Specific Embodiment of the Present Invention

A specific embodiment of the present invention will be detailed hereinafter referring to the attached drawings. A CMOS transistor is exemplified herein as the semiconductor device, and the configuration thereof, together with a method of fabrication, will be described for the convenience sake.

FIGS. 2A to 5B are schematic sectional views sequentially showing process steps of a method of fabricating the CMOS transistor of the present embodiment.

First as shown in FIG. 2A, an element isolation structure 12 is formed in the element isolation region of a p-type silicon semiconductor substrate 11 by the STI (shallow trench isolation) process, in which grooves herein are formed as the element isolation structure and are then filled with an insulating material, to thereby define active regions 13 a, 13 b. The active region 13 a herein serves as a formation region for an nMOS transistor, and the active region 13 b serves as a formation region for a pMOS transistor. The active regions 13 a and 13 b are then implanted with a p-type impurity and an n-type impurity, respectively, to thereby form a p-type well 14 a and an n-type well 14 b.

Next, as shown in FIG. 2B, a gate insulating film 15 composed of silicon oxynitrides is formed by the thermal nitridation on the surface of the p-type well 14 a and n-type well 14 b, a polysilicon film is deposited thereon by the CVD process, and the polysilicon film (together with the gate insulating film 15) is then patterned by photolithography and succeeding dry etching, to thereby form a gate electrode 16. The gate insulating film 15 herein may be composed of silicon oxide.

Next, an extension region and a pocket region are formed in the active region 13 a.

More specifically, as shown in FIG. 2C, the active region 13 b is covered with a photo-resist 31, and an n-type impurity, which is arsenic (As) herein, is implanted into the surficial layer of the active region 13 a, under masking by the gate electrode 16 and the photo-resist 31, and under conditions of an ion acceleration energy of 1 keV to 5 keV, a dose of 5×10¹⁴/cm² to 2×10¹⁵/cm² and an angle of inclination (an angle away from the normal line on the substrate surface) of 0°, to thereby form an extension region 17 a.

Next, a p-type impurity, which is indium (In) herein, is implanted into the surficial layer of the active region 13 a, similarly under masking by the gate electrode 16 and the photo-resist 31, and under conditions of an ion acceleration energy of 30 keV to 100 keV, a dose of 5×10¹²/cm² to 1.5×10¹³/cm² and an angle of inclination of 0° to 45° from four directions (4 times of ion implantation), to thereby form a pocket region 18 a. The photo-resist 31 is thereafter removed typically by ashing.

Next, the extension region and the pocket region are formed also in the active region 13 b.

More specifically, as shown in FIG. 3A, the active region 13 a is covered with a photo-resist 32, and a p-type impurity, which is boron (B) herein, is implanted into the surficial layer of the active region 13 b, under masking by the gate electrode 16 and the photo-resist 32, and under conditions of an ion acceleration energy of 0.1 keV to 1 keV, a dose of 5×10¹⁴/cm² to 2×10¹⁵/cm² and an angle of inclination of 0°, to thereby form an extension region 17 b.

Next, an n-type impurity, which is antimony (Sb) herein, is implanted into the surficial layer of the active region 13 b, similarly under masking by the gate electrode 16 and the photo-resist 32, and under conditions of an ion acceleration energy of 30 keV to 100 keV, a dose of 5×10¹²/cm² to 1.5×10¹³/cm² and an angle of inclination of 0° to 45° from four directions (4 times of ion implantation), to thereby form a pocket region 18 b. The photo-resist 32 is thereafter removed typically by ashing.

Next, as shown in FIG. 3B, a silicon oxide film is deposited over the entire surface of the semiconductor substrate 1 including the active regions 13 a, 13 b, and the entire surface of the silicon oxide film is then anisotropically etched (etchback) so as to leave the silicon oxide film only on both lateral faces of the gate electrode 16, to thereby form a first sidewall spacer 19 to a thickness of approximately 10 nm to 50 nm. The insulating film composing the first sidewall spacer 19 herein is preferably composed of a material formed under a temperature condition not causative of diffusion of the impurity contained in the previously-formed extension regions 17 a, 17 b and the pocket regions 18 a, 18 b, and is preferably formed at the same temperature. More specifically, BTBAS (bis-tertiary-butylaminosilane) and oxygen can typically be used, where the silicon oxide film is formed by the thermal CVD process at a filming temperature ranging from 500° C. to 580° C., and a filming time ranging from 5 minutes to 20 minutes.

Next, the diffusion suppressive region is formed in the active region 13 a.

More specifically, as shown in FIG. 3C, the active region 13 b is covered with a photo-resist 33, and a diffusion suppressive element, which is arsenic (As) herein, is implanted into the surficial layer of the active region 13 a, under masking by the gate electrode 16, the first sidewall spacer 19 and the photo-resist 33, and under conditions of an ion acceleration energy of 3 keV to 15 keV, a dose of 5×10¹⁴/cm² to 3×10¹⁵/cm² and an angle of inclination of 0°, to thereby form an amorphous diffusion suppressive region 20 a. The photo-resist 33 is thereafter removed typically by ashing.

Next, the diffusion suppressive region is formed also in the active region 13 b.

More specifically, as shown in FIG. 4A, the active region 13 a is covered with a photo-resist 34, and a diffusion suppressive element, which is germanium (Ge) herein, is implanted into the surficial layer of the active region 13 b, under masking by the gate electrode 16, the first sidewall spacer 19 and the photo-resist 34, and under conditions of an ion acceleration energy of 3 keV to 15 keV, a dose of 5×10¹⁴/cm² to 3×10¹⁵/cm² and an angle of inclination of 0°, to thereby form an amorphous diffusion suppressive region 20 b. It is also allowable herein to implant p-type impurity ion such as boron(B) in addition to Ge. The photo-resist 34 is thereafter removed typically by ashing.

Next, as shown in FIG. 4B, a silicon oxide film is deposited over the entire surface of the semiconductor substrate 1 including the active regions 13 a, 13 b, and the entire surface of the silicon oxide film is then anisotropically etched (etchback) so as to leave the silicon oxide film only on both lateral faces of the gate electrode 16 and so as to cover the first sidewall spacer 19, to thereby form a second sidewall spacer 21 to a thickness of approximately 50 nm to 100 nm. The insulating film composing the second sidewall spacer 21 herein is preferably composed of a material formed under a temperature condition not causative of re-crystallization of the previously-formed diffusion suppressive regions 20 a, 20 b, and is preferably formed at the same temperature. More specifically, BTBAS (bis-tertiary-butylaminosilane) and oxygen can typically be used, where the silicon oxide film is formed by the thermal CVD process at a filming temperature ranging from 500° C. to 580° C., and a filming time ranging from 5 minutes to 20 minutes.

Next, the source-and-drain having a deep junction is formed in the active region 13 a.

More specifically, as shown in FIG. 4C, the active region 13 b is covered with a photo-resist 35, and an n-type impurity, which is phosphorus (P) herein, is implanted into the surficial layer of the active region 13 b, under masking by the gate electrode 16, the first sidewall spacer 19, the second sidewall spacer 21 and the photo-resist 35, and under conditions of an ion acceleration energy of 4 keV to 10 keV, a dose of as large as 4×10¹⁵/cm² to 1.5×10¹⁶/cm² and an angle of inclination of 0°, to thereby form a source-and-drain 22 a. It is also allowable herein to implant germanium (Ge) for example before the P implantation. The photo-resist 35 is thereafter removed typically by ashing.

Next, the source-and-drain having a deep junction is formed also in the active region 13 b.

More specifically, as shown in FIG. 5A, the active region 13 a is covered with a photo-resist 36, and a p-type impurity, which is boron (B) herein, is implanted into the surficial layer of the active region 13 b, under masking by the gate electrode 16, the first sidewall spacer 19, the second sidewall spacer 21 and the photo-resist 36, and under conditions of an ion acceleration energy of 2 keV to 5 keV, a dose of as large as 4×10¹⁵/cm² to 1.5×10¹⁶/cm² and an angle of inclination of 0°, to thereby form a source-and-drain 22 b. It is also allowable herein to implant germanium (Ge) for example before the B implantation. The photo-resist 36 is thereafter removed typically by ashing.

Next, spike annealing is carried out at 1000° C. to 1070° C. in an N₂ atmosphere to thereby activate the n-type impurity and p-type impurity previously introduced.

Next, as shown in FIG. 5B, a silicide-forming metal, which is Co or Ni for example, is deposited over the entire surface, and allowed the metal to react with silicon under annealing so as to proceed self-aligned silicidation (SALICIDE), to thereby form a silicide layer 23, which is composed of CoSi or NiSi for example, on the gate electrode 16 and source-and-drains 22 a, 22 b. Unreacted residue of the silicide-forming metal is then removed.

A MOS transistor is finished after formation of an interlayer insulating film covering the entire surface, and various wiring processes.

Using thus-fabricated MOS transistor having a gate length of 40 nm, various transistor characteristics were examined. Results are described below.

FIG. 6 shows roll-off characteristics expressed by relations between gate length L_(g) and threshold voltage; FIG. 7 shows C_(ov) characteristics expressed by relations between depth of diffusion suppressive region and C_(ovn); and FIG. 8 shows I_(on)-I_(off) characteristics expressed by relations between ON current (I_(on)) and OFF current (I_(off)). It is obvious that adoption of the diffusion suppressive region is successful in improving the roll-off characteristics, and in improving the drive current through reduction in C_(ov) and parasitic resistance right under the second sidewall spacer.

The present invention is successful in exactly suppressing lateral diffusion of the source-and-drain, fulfilling further demands for micronization and advanced performances, and consequently realizing a highly-reliable semiconductor device. 

1. A semiconductor device comprising: a gate formed over a semiconductor region; a first impurity-diffused region formed, as being aligned with said gate, in a surficial layer of said semiconductor region and having a first depth; a second impurity-diffused region formed, as being distant from said gate with a first distance and having a second depth; and a third impurity-diffused region formed, as being distant from said gate with a second distance and having a third depth; wherein the third depth is larger than the first depth, and the second depth is larger than the third depth, wherein the second distance is longer than the third distance, wherein said second impurity-diffused region is formed containing at least any one selected from germanium, nitrogen, fluorine and carbon for the case where the impurity contained in the first and the second impurity-diffused regions in an n-type impurity.
 2. The semiconductor device according to claim 1, further comprising: a first sidewall spacer formed over both lateral faces of said gate; and a second sidewall spacer formed to cover said first sidewall spacer over both lateral sides of said gate; wherein said second impurity-diffused region is formed as being aligned with said second sidewall spacer, and said third impurity-diffused region is formed as being aligned with said first sidewall spacer.
 3. The semiconductor device according to claim 1, further comprising a fourth impurity-diffused region formed, in the surficial layer of said semiconductor region, as being aligned with said gate and as containing an impurity having a conductivity type opposite to that of impurities contained in said first and third impurity-diffused regions. 